HDPE BU7100 resin
HDPE large-part blow molding · Lotte Chemical
Univation gas-phase process; high melt strength, excellent formability and ESCR. Thien An Plastics supplies BU7100 in original bags to manufacturers in Vietnam and for export.
- Producer (per TDS)
- Lotte Chemical (Lotte BU7100)
- Polymer
- HDPE – High-density polyethylene
- Type
- HDPE large-part blow molding
- Processing
- Blow molding
What is BU7100?
HDPE BU7100 from Lotte Chemical is a HDPE large-part blow molding, high-load melt index (190 °C/21.6 kg): 10 g/10 min; density: 0.948 g/cm³. BU7100 is typically used for: large industrial containers and drums, jerricans, large blow-molded parts (buoys, median strips). Thien An Plastics (Hanoi, Vietnam) supplies BU7100 in original bags with TDS; quotes via WhatsApp/WeChat/Zalo +84 389 980 742.
Also searched as: Lotte BU7100, HDPE BU7100, BU 7100, Lotte BU7100
Applications
- Large industrial containers and drums
- Jerricans
- Large blow-molded parts (buoys, median strips)
Typical properties – BU7100
| Property | Value | Unit |
|---|---|---|
| High-load melt index (190 °C/21.6 kg) | 10 | g/10 min |
| Density | 0.948 | g/cm³ |
| Tensile strength at yield | 260 | kg/cm² |
| Flexural modulus | 11200 | kg/cm² |
| Environmental stress crack resistance (ESCR) | > 1000 | h |
Typical values from the producer's TDS, for reference only and not specifications. Producer and lot may vary; please confirm when ordering.
FAQ
What type of plastic is BU7100?
BU7100 (Lotte BU7100) is a HDPE large-part blow molding produced by Lotte Chemical, in the High-density polyethylene (HDPE) family.
What are the melt flow rate and density of BU7100?
High-load melt index (190 °C/21.6 kg): 10 g/10 min; Density: 0.948 g/cm³.
What is BU7100 used for?
BU7100 is typically used for: Large industrial containers and drums, Jerricans, Large blow-molded parts (buoys, median strips).
Where can I buy BU7100 and get its TDS?
Thien An Plastics (Hanoi, Vietnam) supplies BU7100 with its TDS. Contact +84 389 980 742 on WhatsApp, WeChat or Zalo for a quote.